Titanium enterprise security and industry-specific requirements

Titanium enterprise security and industry-specific requirements

7.1 Safe Production

1. Titanium companies should develop and implement safe systems of production in accordance with relevant laws and regulations. titanium sheet price enterprise's production facilities, dangerous parts of the equipment shall have safety guards, workshops, warehouses and other places should be equipped with fire-fighting equipment, flammable, explosive and other dangerous goods should be isolated and protection.

2.Does titanium production of safety systems.

3.Does dangerous parts necessary protective measures.

4.workshops, warehouses, etc. are equipped with fire fighting equipment, fire equipment is within the validity period.

5.Is flammable, explosive and other dangerous goods isolation and protection.


6. Smelting furnace should have proof facilities.

Smelting furnace explosion facility meets the safety requirements or whether there is evidence of safety materials, equipment design and manufacturing units.



7.2

Labor Protection

titanium round bar enterprises to cope with staff training in production safety and labor protection, and to provide the necessary labor protection for employees.

1. whether the necessary production safety and labor protection training.

2. whether to provide the necessary labor protection.

3. The employees of the production operations conform to safety regulations.

7.3 *


Industry-specific requirements


Waste water, waste gas and waste treatment shall comply with the requirements of environmental protection department.
Waste water, waste gas and waste treatment is compliance.

titanium welding wire operation essentials

1, manual welding, weldment between the wire and should be kept to a minimum angle (10 ~ 15 °).medical titanium alloy Wire along the pool front smooth, uniform into the pool, not the end of the wire out of the argon gas reserves.
2, titanium welding wire welding torch without substantially horizontal swing, the swing when required, the frequency is lower,Medical titanium bar the swing amplitude is not too large, in order to prevent the effects of the protection of argon.
3, when the arc and weld finishing off, to continue through argon, until the weld metal and heat affected zone is cooled to remove the gun before the time below 350 ℃.

titanium wires Introduction

In the oxygen-rich conditions must take into account the effects of oxygen absorption hardening depth .  Only under conditions of thin layer thickness in a vacuum or in argon - methane atmosphere,grade 3 titanium it may penetrate the toner to form a sufficient adhesive strength as compared with this, using a gas  agent may form hard and particularly good adhesion titanium carbide hardened layer. While the: and 10201: conditions at temperatures between formation and hardening exhibition in between.medical titanium bar With increasing thickness of the titanium carbide layer becomes more brittle and tend to peel t To avoid leaving alkyl decomposition of carbon inclusions invasion of titanium carbide layer should be about 2% volume fraction of the provisions Rui alkyl dose additive gas  in an inert gas. When using propane, methane and the use of additives on the formation of  when low surface hardness. When the adhesive force reaches Wu Mao  conditions when using propane gas although the measured thickness of the hardened layer is very thin, but it has the best wear resistance. Absorption of hydrogen in the gas  agent type conditions using either, but had to remove it again when the vacuum annealing
.